Recently, it has been learned from the feedback from customers that many use of shot blasting machines ignores the use of shot blasting machine accessories, resulting in excessive loss and breakage of the parts, resulting in the inability of the machine to operate and causing unnecessary losses to the company. Ten thousand can not be underestimated the role of shot blasting machine accessories, the quality of the accessories in the shot blasting machine can be related to the overall quality of the shot blasting machine. When using the shot blasting machine, paying more attention to the fittings is equivalent to extending the blasting in disguise. Machine life and shot blast quality. Thereby controlling the production cost of the enterprise and improving the existence value of the shot blasting machine.

Maintenance of shot blasting machine parts in high temperature and high humidity environment

In the environment with high temperature and high humidity, when the shot blasting machine is in use, the reducer, motor, blade, etc. are more likely to generate heat, and the temperature of the air itself is high, and the heat of the shot blasting machine is not easy to heat up. In this case, the consumption of shot blasting machine parts will increase exponentially. Since the shot blasting machine itself is in a rainy, humid and humid environment, the electrical components of the shot blasting machine are aging and easy to be short-circuited. This situation requires special attention. The shot blasting machine uses steel grit to rust easily in a humid environment. The rusted steel grit is easy to damage the blasting machine lifting belt and the shot blasting machine spiral during use.

Therefore, in the high temperature and high humidity environment, the shot blasting machine should be thoroughly inspected, and the parts need to be replaced in time, and each oil filling point should be oiled in time. In the material selection of shot blasting machine parts, materials with high quality, such as shot blasting machine guards, blades, etc., should be made of high chromium. Use high quality grease, use GB bearings and so on. The production workshop should be well ventilated and cooled.

The working time of the shot blasting machine should be reasonably arranged.

Generally speaking, the wear-resistant parts and damage parts of the shot blasting machine are made of high-chromium wear-resistant cast iron. In terms of service life, the service life of the blade is more than 500h, and the side plate and the top plate must be at least 800h, and the end plate It should reach 1200h, the directional sleeve splitting wheel can reach 1800h, and the main body shield of the mainframe is no problem within one year. Some shot blasting machines are still in perfect condition after using for more than 2 years, and some are still in good condition. After three or four months of use, the shot blasting machine showed severe wear and tear on the parts.

In our use, we found that if the shot blasting machine is used continuously for a long time without intermittent use, the steel plate will be heated. In this case, the steel ball will continue to strike on the surface of the wear-resistant part, and the surface will be formed one by one. The concave point, if used for a long time, can make the wear-resistant component of the wear-resistant part drop sharply, causing the wear-resistant part to consume too fast and break, so in the use of the shot blasting machine, we should properly give the shot blasting machine There is a time to cool down, so that the shot blasting machine can maintain a good working condition and thus operate well for a long time.